60Pd-40Ag Alloy vs. N08810 Stainless Steel
60Pd-40Ag alloy belongs to the otherwise unclassified metals classification, while N08810 stainless steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is 60Pd-40Ag alloy and the bottom bar is N08810 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 200 |
| Elongation at Break, % | 1.1 to 28 | |
| 33 |
| Poisson's Ratio | 0.38 | |
| 0.28 |
| Shear Modulus, GPa | 37 | |
| 77 |
| Shear Strength, MPa | 220 to 350 | |
| 340 |
| Tensile Strength: Ultimate (UTS), MPa | 340 to 720 | |
| 520 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 300 |
| Melting Completion (Liquidus), °C | 1360 | |
| 1400 |
| Melting Onset (Solidus), °C | 1310 | |
| 1350 |
| Specific Heat Capacity, J/kg-K | 240 | |
| 480 |
| Thermal Conductivity, W/m-K | 29 | |
| 12 |
| Thermal Expansion, µm/m-K | 15 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 4.1 | |
| 1.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.2 | |
| 1.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 11 | |
| 8.0 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.9 | |
| 14 |
| Stiffness to Weight: Bending, points | 14 | |
| 24 |
| Strength to Weight: Axial, points | 8.4 to 18 | |
| 18 |
| Strength to Weight: Bending, points | 9.6 to 16 | |
| 18 |
| Thermal Diffusivity, mm2/s | 11 | |
| 3.0 |
| Thermal Shock Resistance, points | 16 to 34 | |
| 13 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0.15 to 0.6 |
| Carbon (C), % | 0 | |
| 0.050 to 0.1 |
| Chromium (Cr), % | 0 | |
| 19 to 23 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 to 0.75 |
| Iron (Fe), % | 0 | |
| 39.5 to 50.7 |
| Manganese (Mn), % | 0 | |
| 0 to 1.5 |
| Nickel (Ni), % | 0 | |
| 30 to 35 |
| Palladium (Pd), % | 59.5 to 60.9 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Silver (Ag), % | 39.1 to 40.5 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 0.15 to 0.6 |
| Residuals, % | 0 to 0.3 | |
| 0 |