6005 Aluminum vs. 5454 Aluminum
Both 6005 aluminum and 5454 aluminum are aluminum alloys. They have a very high 97% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is 6005 aluminum and the bottom bar is 5454 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 90 to 95 | |
| 61 to 93 |
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 69 |
| Elongation at Break, % | 9.5 to 17 | |
| 2.3 to 18 |
| Fatigue Strength, MPa | 55 to 95 | |
| 83 to 160 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 120 to 210 | |
| 140 to 200 |
| Tensile Strength: Ultimate (UTS), MPa | 190 to 310 | |
| 230 to 350 |
| Tensile Strength: Yield (Proof), MPa | 100 to 280 | |
| 97 to 290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 190 |
| Melting Completion (Liquidus), °C | 650 | |
| 650 |
| Melting Onset (Solidus), °C | 610 | |
| 600 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 180 to 200 | |
| 130 |
| Thermal Expansion, µm/m-K | 23 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 54 | |
| 34 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 180 | |
| 110 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 8.6 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1180 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 27 to 36 | |
| 6.3 to 34 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 77 to 550 | |
| 68 to 590 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 51 | |
| 50 |
| Strength to Weight: Axial, points | 20 to 32 | |
| 23 to 36 |
| Strength to Weight: Bending, points | 28 to 38 | |
| 30 to 41 |
| Thermal Diffusivity, mm2/s | 74 to 83 | |
| 55 |
| Thermal Shock Resistance, points | 8.6 to 14 | |
| 10 to 16 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 97.5 to 99 | |
| 94.5 to 97.1 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0.050 to 0.2 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.35 | |
| 0 to 0.4 |
| Magnesium (Mg), % | 0.4 to 0.6 | |
| 2.4 to 3.0 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0.5 to 1.0 |
| Silicon (Si), % | 0.6 to 0.9 | |
| 0 to 0.25 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 to 0.25 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.15 |