6016 Aluminum vs. Grade Ti-Pd7B Titanium
6016 aluminum belongs to the aluminum alloys classification, while grade Ti-Pd7B titanium belongs to the titanium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is 6016 aluminum and the bottom bar is grade Ti-Pd7B titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 55 to 80 | |
| 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 69 | |
| 110 |
| Elongation at Break, % | 11 to 27 | |
| 17 |
| Fatigue Strength, MPa | 68 to 89 | |
| 200 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Shear Modulus, GPa | 26 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 200 to 280 | |
| 390 |
| Tensile Strength: Yield (Proof), MPa | 110 to 210 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 420 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 320 |
| Melting Completion (Liquidus), °C | 660 | |
| 1660 |
| Melting Onset (Solidus), °C | 610 | |
| 1610 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 540 |
| Thermal Conductivity, W/m-K | 190 to 210 | |
| 22 |
| Thermal Expansion, µm/m-K | 23 | |
| 8.7 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 48 to 54 | |
| 3.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 160 to 180 | |
| 7.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.7 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 49 |
| Embodied Energy, MJ/kg | 150 | |
| 840 |
| Embodied Water, L/kg | 1180 | |
| 520 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 29 to 47 | |
| 62 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 82 to 340 | |
| 440 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 51 | |
| 35 |
| Strength to Weight: Axial, points | 21 to 29 | |
| 24 |
| Strength to Weight: Bending, points | 29 to 35 | |
| 26 |
| Thermal Diffusivity, mm2/s | 77 to 86 | |
| 8.9 |
| Thermal Shock Resistance, points | 9.1 to 12 | |
| 30 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 96.4 to 98.8 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.2 |
| Magnesium (Mg), % | 0.25 to 0.6 | |
| 0 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 | |
| 0 to 0.4 |
| Palladium (Pd), % | 0 | |
| 0.12 to 0.3 |
| Silicon (Si), % | 1.0 to 1.5 | |
| 0 |
| Titanium (Ti), % | 0 to 0.15 | |
| 98.8 to 99.9 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.4 |