6016-T4 Aluminum vs. 6082-T4 Aluminum
Both 6016-T4 aluminum and 6082-T4 aluminum are aluminum alloys. Both are furnished in the T4 temper. They have a very high 99% of their average alloy composition in common.
For each property being compared, the top bar is 6016-T4 aluminum and the bottom bar is 6082-T4 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 55 | |
| 58 |
| Elastic (Young's, Tensile) Modulus, GPa | 69 | |
| 69 |
| Elongation at Break, % | 27 | |
| 16 |
| Fatigue Strength, MPa | 68 | |
| 66 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 130 | |
| 140 |
| Tensile Strength: Ultimate (UTS), MPa | 200 | |
| 230 |
| Tensile Strength: Yield (Proof), MPa | 110 | |
| 120 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 170 |
| Melting Completion (Liquidus), °C | 660 | |
| 650 |
| Melting Onset (Solidus), °C | 610 | |
| 580 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 190 | |
| 160 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 48 | |
| 42 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 160 | |
| 140 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 8.3 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1180 | |
| 1170 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 47 | |
| 31 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 82 | |
| 110 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 51 | |
| 50 |
| Strength to Weight: Axial, points | 21 | |
| 24 |
| Strength to Weight: Bending, points | 29 | |
| 31 |
| Thermal Diffusivity, mm2/s | 77 | |
| 67 |
| Thermal Shock Resistance, points | 9.1 | |
| 10 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 96.4 to 98.8 | |
| 95.2 to 98.3 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 to 0.25 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 0.25 to 0.6 | |
| 0.6 to 1.2 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0.4 to 1.0 |
| Silicon (Si), % | 1.0 to 1.5 | |
| 0.7 to 1.3 |
| Titanium (Ti), % | 0 to 0.15 | |
| 0 to 0.1 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 to 0.2 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.15 |