6063 Aluminum vs. 7049A Aluminum
Both 6063 aluminum and 7049A aluminum are aluminum alloys. They have 88% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is 6063 aluminum and the bottom bar is 7049A aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 71 |
| Elongation at Break, % | 7.3 to 21 | |
| 5.0 to 5.7 |
| Fatigue Strength, MPa | 39 to 95 | |
| 180 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Shear Modulus, GPa | 26 | |
| 27 |
| Shear Strength, MPa | 70 to 190 | |
| 340 to 350 |
| Tensile Strength: Ultimate (UTS), MPa | 110 to 300 | |
| 580 to 590 |
| Tensile Strength: Yield (Proof), MPa | 49 to 270 | |
| 500 to 530 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 370 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 200 |
| Melting Completion (Liquidus), °C | 650 | |
| 640 |
| Melting Onset (Solidus), °C | 620 | |
| 430 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 850 |
| Thermal Conductivity, W/m-K | 190 to 220 | |
| 130 |
| Thermal Expansion, µm/m-K | 23 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 49 to 58 | |
| 40 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 160 to 190 | |
| 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 10 |
| Density, g/cm3 | 2.7 | |
| 3.1 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 8.2 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1190 | |
| 1100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 to 27 | |
| 28 to 32 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 18 to 540 | |
| 1800 to 1990 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 50 | |
| 44 |
| Strength to Weight: Axial, points | 11 to 31 | |
| 52 to 53 |
| Strength to Weight: Bending, points | 18 to 37 | |
| 50 to 51 |
| Thermal Diffusivity, mm2/s | 79 to 89 | |
| 50 |
| Thermal Shock Resistance, points | 4.8 to 13 | |
| 25 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 97.5 to 99.4 | |
| 84.6 to 89.5 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0.050 to 0.25 |
| Copper (Cu), % | 0 to 0.1 | |
| 1.2 to 1.9 |
| Iron (Fe), % | 0 to 0.35 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 0.45 to 0.9 | |
| 2.1 to 3.1 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 to 0.5 |
| Silicon (Si), % | 0.2 to 0.6 | |
| 0 to 0.4 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 to 0.25 |
| Zinc (Zn), % | 0 to 0.1 | |
| 7.2 to 8.4 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.25 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.15 |