60Cr-40Ni Alloy vs. EN 1.4028 Stainless Steel

60Cr-40Ni alloy belongs to the otherwise unclassified metals classification, while EN 1.4028 stainless steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is 60Cr-40Ni alloy and the bottom bar is EN 1.4028 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Poisson's Ratio 0.25
0.28
Shear Modulus, GPa 87
76
Tensile Strength: Ultimate (UTS), MPa 870
660 to 930
Tensile Strength: Yield (Proof), MPa 660
390 to 730

Thermal Properties

Latent Heat of Fusion, J/g 370
270
Specific Heat Capacity, J/kg-K 490
480
Thermal Expansion, µm/m-K 16
11

Otherwise Unclassified Properties

Base Metal Price, % relative 49
7.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 7.4
1.9
Embodied Energy, MJ/kg 110
27
Embodied Water, L/kg 380
100

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 1000
380 to 1360
Stiffness to Weight: Axial, points 16
14
Stiffness to Weight: Bending, points 26
25
Strength to Weight: Axial, points 31
24 to 33
Strength to Weight: Bending, points 26
22 to 27
Thermal Shock Resistance, points 18
23 to 32

Alloy Composition

Aluminum (Al), % 0 to 0.25
0
Carbon (C), % 0 to 0.1
0.26 to 0.35
Chromium (Cr), % 58 to 62
12 to 14
Iron (Fe), % 0 to 1.0
83.1 to 87.7
Manganese (Mn), % 0 to 0.3
0 to 1.5
Nickel (Ni), % 34.5 to 42
0
Nitrogen (N), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.020
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.020
0 to 0.015
Titanium (Ti), % 0 to 0.5
0