60Cr-40Ni Alloy vs. Grade 16 Titanium
60Cr-40Ni alloy belongs to the otherwise unclassified metals classification, while grade 16 titanium belongs to the titanium alloys. There are 18 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is 60Cr-40Ni alloy and the bottom bar is grade 16 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 110 |
| Poisson's Ratio | 0.25 | |
| 0.32 |
| Shear Modulus, GPa | 87 | |
| 38 |
| Tensile Strength: Ultimate (UTS), MPa | 870 | |
| 400 |
| Tensile Strength: Yield (Proof), MPa | 660 | |
| 340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 420 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 540 |
| Thermal Expansion, µm/m-K | 16 | |
| 9.2 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 7.4 | |
| 36 |
| Embodied Energy, MJ/kg | 110 | |
| 600 |
| Embodied Water, L/kg | 380 | |
| 230 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1000 | |
| 550 |
| Stiffness to Weight: Axial, points | 16 | |
| 13 |
| Stiffness to Weight: Bending, points | 26 | |
| 35 |
| Strength to Weight: Axial, points | 31 | |
| 25 |
| Strength to Weight: Bending, points | 26 | |
| 27 |
| Thermal Shock Resistance, points | 18 | |
| 29 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 to 0.25 | |
| 0 |
| Carbon (C), % | 0 to 0.1 | |
| 0 to 0.080 |
| Chromium (Cr), % | 58 to 62 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 to 1.0 | |
| 0 to 0.3 |
| Manganese (Mn), % | 0 to 0.3 | |
| 0 |
| Nickel (Ni), % | 34.5 to 42 | |
| 0 |
| Nitrogen (N), % | 0 to 0.3 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.25 |
| Palladium (Pd), % | 0 | |
| 0.040 to 0.080 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 |
| Titanium (Ti), % | 0 to 0.5 | |
| 98.8 to 99.96 |
| Residuals, % | 0 | |
| 0 to 0.4 |