60Cr-40Ni Alloy vs. N07716 Nickel

60Cr-40Ni alloy belongs to the otherwise unclassified metals classification, while N07716 nickel belongs to the nickel alloys. They have 60% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is 60Cr-40Ni alloy and the bottom bar is N07716 nickel.

60Cr-40Ni (R20600) Casting Alloy UNS N07716 Nickel Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		220
Elastic (Young's, Tensile) Modulus, GPa		200

Poisson's Ratio		0.25
Poisson's Ratio		0.29

Shear Modulus, GPa		87
Shear Modulus, GPa		78

Tensile Strength: Ultimate (UTS), MPa		870
Tensile Strength: Ultimate (UTS), MPa		860

Tensile Strength: Yield (Proof), MPa		660
Tensile Strength: Yield (Proof), MPa		350

Thermal Properties

Latent Heat of Fusion, J/g		370
Latent Heat of Fusion, J/g		320

Specific Heat Capacity, J/kg-K		490
Specific Heat Capacity, J/kg-K		440

Thermal Expansion, µm/m-K		16
Thermal Expansion, µm/m-K		13

Otherwise Unclassified Properties

Base Metal Price, % relative		49
Base Metal Price, % relative		75

Density, g/cm³		7.8
Density, g/cm³		8.5

Embodied Carbon, kg CO₂/kg material		7.4
Embodied Carbon, kg CO₂/kg material		13

Embodied Energy, MJ/kg		110
Embodied Energy, MJ/kg		190

Embodied Water, L/kg		380
Embodied Water, L/kg		280

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m³		1000
Resilience: Unit (Modulus of Resilience), kJ/m³		300

Stiffness to Weight: Axial, points		16
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		26
Stiffness to Weight: Bending, points		23

Strength to Weight: Axial, points		31
Strength to Weight: Axial, points		28

Strength to Weight: Bending, points		26
Strength to Weight: Bending, points		24

Thermal Shock Resistance, points		18
Thermal Shock Resistance, points		24

Alloy Composition

Aluminum (Al), %		0 to 0.25
Aluminum (Al), %		0 to 0.35

Carbon (C), %		0 to 0.1
Carbon (C), %		0 to 0.030

Chromium (Cr), %		58 to 62
Chromium (Cr), %		19 to 22

Iron (Fe), %		0 to 1.0
Iron (Fe), %		0 to 11.3

Manganese (Mn), %		0 to 0.3
Manganese (Mn), %		0 to 0.2

Molybdenum (Mo), %		0
Molybdenum (Mo), %		7.0 to 9.5

Nickel (Ni), %		34.5 to 42
Nickel (Ni), %		59 to 63

Niobium (Nb), %		0
Niobium (Nb), %		2.8 to 4.0

Nitrogen (N), %		0 to 0.3
Nitrogen (N), %		0

Phosphorus (P), %		0 to 0.020
Phosphorus (P), %		0 to 0.015

Silicon (Si), %		0 to 1.0
Silicon (Si), %		0 to 0.2

Sulfur (S), %		0 to 0.020
Sulfur (S), %		0 to 0.010

Titanium (Ti), %		0 to 0.5
Titanium (Ti), %		1.0 to 1.6