60Cr-40Ni Alloy vs. ZA-12
60Cr-40Ni alloy belongs to the otherwise unclassified metals classification, while ZA-12 belongs to the zinc alloys. There are 19 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is 60Cr-40Ni alloy and the bottom bar is ZA-12.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 83 |
| Poisson's Ratio | 0.25 | |
| 0.26 |
| Shear Modulus, GPa | 87 | |
| 33 |
| Tensile Strength: Ultimate (UTS), MPa | 870 | |
| 260 to 400 |
| Tensile Strength: Yield (Proof), MPa | 660 | |
| 210 to 320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 120 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 450 |
| Thermal Expansion, µm/m-K | 16 | |
| 24 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 49 | |
| 11 |
| Density, g/cm3 | 7.8 | |
| 6.0 |
| Embodied Carbon, kg CO2/kg material | 7.4 | |
| 3.4 |
| Embodied Energy, MJ/kg | 110 | |
| 64 |
| Embodied Water, L/kg | 380 | |
| 440 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1000 | |
| 260 to 620 |
| Stiffness to Weight: Axial, points | 16 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 26 | |
| 24 |
| Strength to Weight: Axial, points | 31 | |
| 12 to 19 |
| Strength to Weight: Bending, points | 26 | |
| 15 to 20 |
| Thermal Shock Resistance, points | 18 | |
| 9.4 to 14 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.25 | |
| 10.5 to 11.5 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0060 |
| Carbon (C), % | 0 to 0.1 | |
| 0 |
| Chromium (Cr), % | 58 to 62 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0.5 to 1.2 |
| Iron (Fe), % | 0 to 1.0 | |
| 0 to 0.075 |
| Lead (Pb), % | 0 | |
| 0 to 0.0060 |
| Magnesium (Mg), % | 0 | |
| 0.015 to 0.030 |
| Manganese (Mn), % | 0 to 0.3 | |
| 0 |
| Nickel (Ni), % | 34.5 to 42 | |
| 0 to 0.020 |
| Nitrogen (N), % | 0 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.060 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.0030 |
| Titanium (Ti), % | 0 to 0.5 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 87.1 to 89 |