6101 Aluminum vs. Titanium 4-4-2
6101 aluminum belongs to the aluminum alloys classification, while titanium 4-4-2 belongs to the titanium alloys. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is 6101 aluminum and the bottom bar is titanium 4-4-2.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 110 |
| Elongation at Break, % | 10 to 25 | |
| 10 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Shear Modulus, GPa | 26 | |
| 42 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 310 |
| Melting Completion (Liquidus), °C | 650 | |
| 1610 |
| Melting Onset (Solidus), °C | 620 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 540 |
| Thermal Conductivity, W/m-K | 220 to 230 | |
| 6.7 |
| Thermal Expansion, µm/m-K | 23 | |
| 8.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 39 |
| Density, g/cm3 | 2.7 | |
| 4.7 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 30 |
| Embodied Energy, MJ/kg | 150 | |
| 480 |
| Embodied Water, L/kg | 1190 | |
| 180 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 50 | |
| 34 |
| Thermal Diffusivity, mm2/s | 89 to 93 | |
| 2.6 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 97.6 to 99.4 | |
| 3.0 to 5.0 |
| Boron (B), % | 0 to 0.060 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.080 |
| Chromium (Cr), % | 0 to 0.030 | |
| 0 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.2 |
| Magnesium (Mg), % | 0.35 to 0.8 | |
| 0 |
| Manganese (Mn), % | 0 to 0.030 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 3.0 to 5.0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 | |
| 0 to 0.25 |
| Silicon (Si), % | 0.3 to 0.7 | |
| 0.3 to 0.7 |
| Tin (Sn), % | 0 | |
| 1.5 to 2.5 |
| Titanium (Ti), % | 0 | |
| 85.8 to 92.2 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 |
| Residuals, % | 0 to 0.1 | |
| 0 to 0.4 |