6101 Aluminum vs. K93600 Alloy
6101 aluminum belongs to the aluminum alloys classification, while K93600 alloy belongs to the iron alloys. There are 13 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 6101 aluminum and the bottom bar is K93600 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 140 |
| Elongation at Break, % | 10 to 25 | |
| 5.0 to 35 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 160 | |
| 440 |
| Melting Onset (Solidus), °C | 620 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 520 |
| Thermal Conductivity, W/m-K | 220 to 230 | |
| 13 |
| Thermal Expansion, µm/m-K | 23 | |
| 7.3 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 57 to 60 | |
| 2.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 190 to 200 | |
| 2.4 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.7 | |
| 8.1 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 9.4 |
| Stiffness to Weight: Bending, points | 50 | |
| 21 |
| Thermal Diffusivity, mm2/s | 89 to 93 | |
| 3.1 |