6101A Aluminum vs. EN 2.4964 Cobalt
6101A aluminum belongs to the aluminum alloys classification, while EN 2.4964 cobalt belongs to the cobalt alloys. There are 27 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 6101A aluminum and the bottom bar is EN 2.4964 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 68 | |
220 |
Elongation at Break, % | 11 | |
40 |
Fatigue Strength, MPa | 80 | |
220 |
Poisson's Ratio | 0.33 | |
0.29 |
Shear Modulus, GPa | 26 | |
86 |
Tensile Strength: Ultimate (UTS), MPa | 220 | |
960 |
Tensile Strength: Yield (Proof), MPa | 190 | |
390 |
Thermal Properties
Latent Heat of Fusion, J/g | 400 | |
290 |
Melting Completion (Liquidus), °C | 640 | |
1630 |
Melting Onset (Solidus), °C | 630 | |
1550 |
Specific Heat Capacity, J/kg-K | 900 | |
400 |
Thermal Conductivity, W/m-K | 200 | |
15 |
Thermal Expansion, µm/m-K | 23 | |
12 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 55 | |
1.9 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 180 | |
1.8 |
Otherwise Unclassified Properties
Density, g/cm3 | 2.7 | |
9.6 |
Embodied Carbon, kg CO2/kg material | 8.3 | |
9.8 |
Embodied Energy, MJ/kg | 150 | |
140 |
Embodied Water, L/kg | 1190 | |
450 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 24 | |
310 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 | |
340 |
Stiffness to Weight: Axial, points | 14 | |
13 |
Stiffness to Weight: Bending, points | 51 | |
21 |
Strength to Weight: Axial, points | 23 | |
28 |
Strength to Weight: Bending, points | 30 | |
23 |
Thermal Diffusivity, mm2/s | 84 | |
3.9 |
Thermal Shock Resistance, points | 10 | |
25 |
Alloy Composition
Aluminum (Al), % | 97.9 to 99.3 | |
0 |
Carbon (C), % | 0 | |
0.050 to 0.15 |
Chromium (Cr), % | 0 | |
19 to 21 |
Cobalt (Co), % | 0 | |
46.4 to 58 |
Copper (Cu), % | 0 to 0.050 | |
0 |
Iron (Fe), % | 0 to 0.4 | |
0 to 3.0 |
Magnesium (Mg), % | 0.4 to 0.9 | |
0 |
Manganese (Mn), % | 0 | |
0 to 2.0 |
Nickel (Ni), % | 0 | |
9.0 to 11 |
Phosphorus (P), % | 0 | |
0 to 0.020 |
Silicon (Si), % | 0.3 to 0.7 | |
0 to 0.4 |
Sulfur (S), % | 0 | |
0 to 0.015 |
Tungsten (W), % | 0 | |
14 to 16 |
Residuals, % | 0 to 0.1 | |
0 |