6101B Aluminum vs. AWS E70C-B2L

6101B aluminum belongs to the aluminum alloys classification, while AWS E70C-B2L belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 6101B aluminum and the bottom bar is AWS E70C-B2L.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
190
Elongation at Break, % 9.1 to 13
21
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 26
73
Tensile Strength: Ultimate (UTS), MPa 190 to 250
580
Tensile Strength: Yield (Proof), MPa 140 to 180
460

Thermal Properties

Latent Heat of Fusion, J/g 400
260
Melting Completion (Liquidus), °C 640
1460
Melting Onset (Solidus), °C 630
1420
Specific Heat Capacity, J/kg-K 900
470
Thermal Conductivity, W/m-K 210
39
Thermal Expansion, µm/m-K 23
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 57
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 190
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
3.0
Density, g/cm3 2.7
7.8
Embodied Carbon, kg CO2/kg material 8.3
1.6
Embodied Energy, MJ/kg 150
22
Embodied Water, L/kg 1190
54

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 20 to 23
110
Resilience: Unit (Modulus of Resilience), kJ/m3 140 to 240
550
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 50
24
Strength to Weight: Axial, points 20 to 25
20
Strength to Weight: Bending, points 27 to 32
20
Thermal Diffusivity, mm2/s 87
11
Thermal Shock Resistance, points 8.5 to 11
17

Alloy Composition

Aluminum (Al), % 98.2 to 99.3
0
Carbon (C), % 0
0 to 0.050
Chromium (Cr), % 0
1.0 to 1.5
Copper (Cu), % 0 to 0.050
0 to 0.35
Iron (Fe), % 0.1 to 0.3
95.1 to 98
Magnesium (Mg), % 0.35 to 0.6
0
Manganese (Mn), % 0 to 0.050
0.4 to 1.0
Molybdenum (Mo), % 0
0.4 to 0.65
Nickel (Ni), % 0
0 to 0.2
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0.3 to 0.6
0.25 to 0.6
Sulfur (S), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.030
Zinc (Zn), % 0 to 0.1
0
Residuals, % 0
0 to 0.5