6101B Aluminum vs. Grade 28 Titanium
6101B aluminum belongs to the aluminum alloys classification, while grade 28 titanium belongs to the titanium alloys. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is 6101B aluminum and the bottom bar is grade 28 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 110 |
| Elongation at Break, % | 9.1 to 13 | |
| 11 to 17 |
| Fatigue Strength, MPa | 62 to 70 | |
| 330 to 480 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Shear Modulus, GPa | 26 | |
| 40 |
| Shear Strength, MPa | 120 to 150 | |
| 420 to 590 |
| Tensile Strength: Ultimate (UTS), MPa | 190 to 250 | |
| 690 to 980 |
| Tensile Strength: Yield (Proof), MPa | 140 to 180 | |
| 540 to 810 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 330 |
| Melting Completion (Liquidus), °C | 640 | |
| 1640 |
| Melting Onset (Solidus), °C | 630 | |
| 1590 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 550 |
| Thermal Conductivity, W/m-K | 210 | |
| 8.3 |
| Thermal Expansion, µm/m-K | 23 | |
| 9.9 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 57 | |
| 1.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 190 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 36 |
| Density, g/cm3 | 2.7 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 37 |
| Embodied Energy, MJ/kg | 150 | |
| 600 |
| Embodied Water, L/kg | 1190 | |
| 370 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 20 to 23 | |
| 87 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 240 | |
| 1370 to 3100 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 50 | |
| 35 |
| Strength to Weight: Axial, points | 20 to 25 | |
| 43 to 61 |
| Strength to Weight: Bending, points | 27 to 32 | |
| 39 to 49 |
| Thermal Diffusivity, mm2/s | 87 | |
| 3.4 |
| Thermal Shock Resistance, points | 8.5 to 11 | |
| 47 to 66 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 98.2 to 99.3 | |
| 2.5 to 3.5 |
| Carbon (C), % | 0 | |
| 0 to 0.080 |
| Copper (Cu), % | 0 to 0.050 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0.1 to 0.3 | |
| 0 to 0.25 |
| Magnesium (Mg), % | 0.35 to 0.6 | |
| 0 |
| Manganese (Mn), % | 0 to 0.050 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.15 |
| Ruthenium (Ru), % | 0 | |
| 0.080 to 0.14 |
| Silicon (Si), % | 0.3 to 0.6 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 92.4 to 95.4 |
| Vanadium (V), % | 0 | |
| 2.0 to 3.0 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 |
| Residuals, % | 0 to 0.1 | |
| 0 to 0.4 |