6105 Aluminum vs. AZ31B Magnesium
6105 aluminum belongs to the aluminum alloys classification, while AZ31B magnesium belongs to the magnesium alloys.
For each property being compared, the top bar is 6105 aluminum and the bottom bar is AZ31B magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 45 |
| Elongation at Break, % | 9.0 to 16 | |
| 5.6 to 12 |
| Fatigue Strength, MPa | 95 to 130 | |
| 100 to 120 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 26 | |
| 17 |
| Shear Strength, MPa | 120 to 170 | |
| 130 to 160 |
| Tensile Strength: Ultimate (UTS), MPa | 190 to 280 | |
| 240 to 270 |
| Tensile Strength: Yield (Proof), MPa | 120 to 270 | |
| 120 to 180 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 350 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 150 |
| Melting Completion (Liquidus), °C | 650 | |
| 600 |
| Melting Onset (Solidus), °C | 600 | |
| 600 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 990 |
| Thermal Conductivity, W/m-K | 180 to 190 | |
| 100 |
| Thermal Expansion, µm/m-K | 23 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 46 to 50 | |
| 18 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 150 to 170 | |
| 95 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 12 |
| Density, g/cm3 | 2.7 | |
| 1.7 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 23 |
| Embodied Energy, MJ/kg | 150 | |
| 160 |
| Embodied Water, L/kg | 1180 | |
| 970 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 25 to 27 | |
| 13 to 25 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 100 to 550 | |
| 170 to 370 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 51 | |
| 70 |
| Strength to Weight: Axial, points | 20 to 29 | |
| 39 to 44 |
| Strength to Weight: Bending, points | 28 to 35 | |
| 50 to 55 |
| Thermal Diffusivity, mm2/s | 72 to 79 | |
| 62 |
| Thermal Shock Resistance, points | 8.6 to 12 | |
| 14 to 16 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 97.2 to 99 | |
| 2.4 to 3.6 |
| Calcium (Ca), % | 0 | |
| 0 to 0.040 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 to 0.050 |
| Iron (Fe), % | 0 to 0.35 | |
| 0 to 0.050 |
| Magnesium (Mg), % | 0.45 to 0.8 | |
| 93.6 to 97.1 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0.050 to 1.0 |
| Nickel (Ni), % | 0 | |
| 0 to 0.0050 |
| Silicon (Si), % | 0.6 to 1.0 | |
| 0 to 0.1 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0.5 to 1.5 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.3 |