6106 Aluminum vs. 6360 Aluminum
Both 6106 aluminum and 6360 aluminum are aluminum alloys. Their average alloy composition is basically identical.
For each property being compared, the top bar is 6106 aluminum and the bottom bar is 6360 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 69 | |
| 68 |
| Elongation at Break, % | 9.1 | |
| 9.0 to 18 |
| Fatigue Strength, MPa | 88 | |
| 31 to 67 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 170 | |
| 76 to 130 |
| Tensile Strength: Ultimate (UTS), MPa | 290 | |
| 120 to 220 |
| Tensile Strength: Yield (Proof), MPa | 220 | |
| 57 to 170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 160 |
| Melting Completion (Liquidus), °C | 660 | |
| 640 |
| Melting Onset (Solidus), °C | 610 | |
| 630 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 190 | |
| 210 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 49 | |
| 54 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 160 | |
| 180 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 8.3 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1190 | |
| 1190 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 24 | |
| 14 to 19 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 370 | |
| 24 to 210 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 50 | |
| 50 |
| Strength to Weight: Axial, points | 29 | |
| 13 to 23 |
| Strength to Weight: Bending, points | 35 | |
| 20 to 30 |
| Thermal Diffusivity, mm2/s | 78 | |
| 86 |
| Thermal Shock Resistance, points | 13 | |
| 5.5 to 9.9 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 97.2 to 99.3 | |
| 97.8 to 99.3 |
| Chromium (Cr), % | 0 to 0.2 | |
| 0 to 0.050 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.15 |
| Iron (Fe), % | 0 to 0.35 | |
| 0.1 to 0.3 |
| Magnesium (Mg), % | 0.4 to 0.8 | |
| 0.25 to 0.45 |
| Manganese (Mn), % | 0.050 to 0.2 | |
| 0.020 to 0.15 |
| Silicon (Si), % | 0.3 to 0.6 | |
| 0.35 to 0.8 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 to 0.1 |
| Zinc (Zn), % | 0 to 0.15 | |
| 0 to 0.1 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.15 |