6110 Aluminum vs. 4045 Aluminum

Both 6110 aluminum and 4045 aluminum are aluminum alloys. They have a moderately high 91% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is 6110 aluminum and the bottom bar is 4045 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 70
71
Elongation at Break, % 2.2
2.3
Fatigue Strength, MPa 120
45
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 26
27
Shear Strength, MPa 290
69
Tensile Strength: Ultimate (UTS), MPa 500
120
Tensile Strength: Yield (Proof), MPa 500
64

Thermal Properties

Latent Heat of Fusion, J/g 410
540
Maximum Temperature: Mechanical, °C 170
160
Melting Completion (Liquidus), °C 640
600
Melting Onset (Solidus), °C 600
580
Specific Heat Capacity, J/kg-K 900
900
Thermal Conductivity, W/m-K 170
170
Thermal Expansion, µm/m-K 23
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 42
45
Electrical Conductivity: Equal Weight (Specific), % IACS 140
160

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
9.5
Density, g/cm3 2.8
2.6
Embodied Carbon, kg CO2/kg material 8.2
7.8
Embodied Energy, MJ/kg 150
150
Embodied Water, L/kg 1170
1070

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 11
2.4
Resilience: Unit (Modulus of Resilience), kJ/m3 1770
29
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 50
54
Strength to Weight: Axial, points 51
13
Strength to Weight: Bending, points 51
21
Thermal Diffusivity, mm2/s 67
74
Thermal Shock Resistance, points 22
5.7

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 94.4 to 98.4
87.4 to 91
Chromium (Cr), % 0.040 to 0.25
0
Copper (Cu), % 0.2 to 0.7
0 to 0.3
Iron (Fe), % 0 to 0.8
0 to 0.8
Magnesium (Mg), % 0.5 to 1.1
0 to 0.050
Manganese (Mn), % 0.2 to 0.7
0 to 0.050
Silicon (Si), % 0.7 to 1.5
9.0 to 11
Titanium (Ti), % 0 to 0.15
0 to 0.2
Zinc (Zn), % 0 to 0.3
0 to 0.1
Residuals, % 0 to 0.15
0 to 0.15