6110 Aluminum vs. AWS BAg-8a

6110 aluminum belongs to the aluminum alloys classification, while AWS BAg-8a belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 6110 aluminum and the bottom bar is AWS BAg-8a.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 70
83
Poisson's Ratio 0.33
0.36
Shear Modulus, GPa 26
31
Tensile Strength: Ultimate (UTS), MPa 500
150

Thermal Properties

Latent Heat of Fusion, J/g 410
140
Melting Completion (Liquidus), °C 640
770
Melting Onset (Solidus), °C 600
770
Specific Heat Capacity, J/kg-K 900
290
Thermal Expansion, µm/m-K 23
19

Otherwise Unclassified Properties

Density, g/cm3 2.8
10

Common Calculations

Stiffness to Weight: Axial, points 14
4.6
Stiffness to Weight: Bending, points 50
15
Strength to Weight: Axial, points 51
4.2
Strength to Weight: Bending, points 51
6.3
Thermal Shock Resistance, points 22
6.7

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 94.4 to 98.4
0
Chromium (Cr), % 0.040 to 0.25
0
Copper (Cu), % 0.2 to 0.7
26.4 to 28.8
Iron (Fe), % 0 to 0.8
0
Lithium (Li), % 0
0.25 to 0.5
Magnesium (Mg), % 0.5 to 1.1
0
Manganese (Mn), % 0.2 to 0.7
0
Silicon (Si), % 0.7 to 1.5
0
Silver (Ag), % 0
71 to 73
Titanium (Ti), % 0 to 0.15
0
Zinc (Zn), % 0 to 0.3
0
Residuals, % 0 to 0.15
0 to 0.15