6110 Aluminum vs. EN AC-41000 Aluminum

Both 6110 aluminum and EN AC-41000 aluminum are aluminum alloys. Their average alloy composition is basically identical. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is 6110 aluminum and the bottom bar is EN AC-41000 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 70
69
Elongation at Break, % 2.2
4.5
Fatigue Strength, MPa 120
58 to 71
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 26
26
Tensile Strength: Ultimate (UTS), MPa 500
170 to 280
Tensile Strength: Yield (Proof), MPa 500
80 to 210

Thermal Properties

Latent Heat of Fusion, J/g 410
420
Maximum Temperature: Mechanical, °C 170
170
Melting Completion (Liquidus), °C 640
640
Melting Onset (Solidus), °C 600
630
Specific Heat Capacity, J/kg-K 900
900
Thermal Conductivity, W/m-K 170
170
Thermal Expansion, µm/m-K 23
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 42
38
Electrical Conductivity: Equal Weight (Specific), % IACS 140
130

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
9.5
Density, g/cm3 2.8
2.7
Embodied Carbon, kg CO2/kg material 8.2
8.2
Embodied Energy, MJ/kg 150
150
Embodied Water, L/kg 1170
1160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 11
6.4 to 11
Resilience: Unit (Modulus of Resilience), kJ/m3 1770
46 to 300
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 50
51
Strength to Weight: Axial, points 51
18 to 29
Strength to Weight: Bending, points 51
26 to 35
Thermal Diffusivity, mm2/s 67
69
Thermal Shock Resistance, points 22
7.8 to 13

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 94.4 to 98.4
95.2 to 97.6
Chromium (Cr), % 0.040 to 0.25
0
Copper (Cu), % 0.2 to 0.7
0 to 0.1
Iron (Fe), % 0 to 0.8
0 to 0.6
Lead (Pb), % 0
0 to 0.050
Magnesium (Mg), % 0.5 to 1.1
0.45 to 0.65
Manganese (Mn), % 0.2 to 0.7
0.3 to 0.5
Nickel (Ni), % 0
0 to 0.050
Silicon (Si), % 0.7 to 1.5
1.6 to 2.4
Tin (Sn), % 0
0 to 0.050
Titanium (Ti), % 0 to 0.15
0.050 to 0.2
Zinc (Zn), % 0 to 0.3
0 to 0.1
Residuals, % 0 to 0.15
0 to 0.15