MakeItFrom.com
Menu (ESC)

6110 Aluminum vs. Grade 1 Babbitt Metal

6110 aluminum belongs to the aluminum alloys classification, while grade 1 Babbitt Metal belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 6110 aluminum and the bottom bar is grade 1 Babbitt Metal.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 70
53
Elongation at Break, % 2.2
34
Poisson's Ratio 0.33
0.35
Shear Modulus, GPa 26
20
Tensile Strength: Yield (Proof), MPa 500
30

Thermal Properties

Latent Heat of Fusion, J/g 410
70
Melting Completion (Liquidus), °C 640
370
Melting Onset (Solidus), °C 600
220
Specific Heat Capacity, J/kg-K 900
230
Thermal Conductivity, W/m-K 170
45
Thermal Expansion, µm/m-K 23
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 42
13
Electrical Conductivity: Equal Weight (Specific), % IACS 140
16

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
75
Density, g/cm3 2.8
7.3
Embodied Carbon, kg CO2/kg material 8.2
12
Embodied Energy, MJ/kg 150
200
Embodied Water, L/kg 1170
1160

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 1770
8.6
Stiffness to Weight: Axial, points 14
4.0
Stiffness to Weight: Bending, points 50
17
Thermal Diffusivity, mm2/s 67
26

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 94.4 to 98.4
0 to 0.0050
Antimony (Sb), % 0
4.0 to 5.0
Arsenic (As), % 0
0 to 0.1
Bismuth (Bi), % 0
0 to 0.080
Cadmium (Cd), % 0
0 to 0.050
Chromium (Cr), % 0.040 to 0.25
0
Copper (Cu), % 0.2 to 0.7
4.0 to 5.0
Iron (Fe), % 0 to 0.8
0 to 0.080
Lead (Pb), % 0
0 to 0.35
Magnesium (Mg), % 0.5 to 1.1
0
Manganese (Mn), % 0.2 to 0.7
0
Silicon (Si), % 0.7 to 1.5
0
Tin (Sn), % 0
89.3 to 92
Titanium (Ti), % 0 to 0.15
0
Zinc (Zn), % 0 to 0.3
0 to 0.0050
Residuals, % 0 to 0.15
0