6110 Aluminum vs. Grade CW12MW Nickel

6110 aluminum belongs to the aluminum alloys classification, while grade CW12MW nickel belongs to the nickel alloys. There are 25 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 6110 aluminum and the bottom bar is grade CW12MW nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 70
220
Elongation at Break, % 2.2
4.6
Fatigue Strength, MPa 120
130
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 26
85
Tensile Strength: Ultimate (UTS), MPa 500
560
Tensile Strength: Yield (Proof), MPa 500
310

Thermal Properties

Latent Heat of Fusion, J/g 410
320
Maximum Temperature: Mechanical, °C 170
960
Melting Completion (Liquidus), °C 640
1610
Melting Onset (Solidus), °C 600
1560
Specific Heat Capacity, J/kg-K 900
410
Thermal Expansion, µm/m-K 23
12

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
70
Density, g/cm3 2.8
9.1
Embodied Carbon, kg CO2/kg material 8.2
13
Embodied Energy, MJ/kg 150
180
Embodied Water, L/kg 1170
280

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 11
22
Resilience: Unit (Modulus of Resilience), kJ/m3 1770
220
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 50
22
Strength to Weight: Axial, points 51
17
Strength to Weight: Bending, points 51
17
Thermal Shock Resistance, points 22
16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 94.4 to 98.4
0
Carbon (C), % 0
0 to 0.12
Chromium (Cr), % 0.040 to 0.25
15.5 to 17.5
Copper (Cu), % 0.2 to 0.7
0
Iron (Fe), % 0 to 0.8
4.5 to 7.5
Magnesium (Mg), % 0.5 to 1.1
0
Manganese (Mn), % 0.2 to 0.7
0 to 1.0
Molybdenum (Mo), % 0
16 to 18
Nickel (Ni), % 0
49.2 to 60.1
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0.7 to 1.5
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Titanium (Ti), % 0 to 0.15
0
Tungsten (W), % 0
3.8 to 5.3
Vanadium (V), % 0
0.2 to 0.4
Zinc (Zn), % 0 to 0.3
0
Residuals, % 0 to 0.15
0