6110 Aluminum vs. Grade Ti-Pd17 Titanium

6110 aluminum belongs to the aluminum alloys classification, while grade Ti-Pd17 titanium belongs to the titanium alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is 6110 aluminum and the bottom bar is grade Ti-Pd17 titanium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 70
110
Elongation at Break, % 2.2
22
Fatigue Strength, MPa 120
140
Poisson's Ratio 0.33
0.32
Shear Modulus, GPa 26
40
Tensile Strength: Ultimate (UTS), MPa 500
270
Tensile Strength: Yield (Proof), MPa 500
190

Thermal Properties

Latent Heat of Fusion, J/g 410
420
Maximum Temperature: Mechanical, °C 170
320
Melting Completion (Liquidus), °C 640
1660
Melting Onset (Solidus), °C 600
1610
Specific Heat Capacity, J/kg-K 900
540
Thermal Conductivity, W/m-K 170
21
Thermal Expansion, µm/m-K 23
8.7

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 42
3.6
Electrical Conductivity: Equal Weight (Specific), % IACS 140
7.1

Otherwise Unclassified Properties

Density, g/cm3 2.8
4.5
Embodied Carbon, kg CO2/kg material 8.2
36
Embodied Energy, MJ/kg 150
600
Embodied Water, L/kg 1170
230

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 11
55
Resilience: Unit (Modulus of Resilience), kJ/m3 1770
180
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 50
35
Strength to Weight: Axial, points 51
17
Strength to Weight: Bending, points 51
21
Thermal Diffusivity, mm2/s 67
8.8
Thermal Shock Resistance, points 22
21

Alloy Composition

Aluminum (Al), % 94.4 to 98.4
0
Carbon (C), % 0
0 to 0.1
Chromium (Cr), % 0.040 to 0.25
0
Copper (Cu), % 0.2 to 0.7
0
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 0 to 0.8
0 to 0.2
Magnesium (Mg), % 0.5 to 1.1
0
Manganese (Mn), % 0.2 to 0.7
0
Nickel (Ni), % 0
0 to 0.030
Oxygen (O), % 0
0 to 0.25
Palladium (Pd), % 0
0.040 to 0.080
Silicon (Si), % 0.7 to 1.5
0
Titanium (Ti), % 0 to 0.15
98.9 to 99.96
Zinc (Zn), % 0 to 0.3
0
Residuals, % 0 to 0.15
0 to 0.4