6110 Aluminum vs. Titanium 15-3-3-3

6110 aluminum belongs to the aluminum alloys classification, while titanium 15-3-3-3 belongs to the titanium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is 6110 aluminum and the bottom bar is titanium 15-3-3-3.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 70
100
Elongation at Break, % 2.2
5.7 to 8.0
Fatigue Strength, MPa 120
610 to 710
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 26
39
Shear Strength, MPa 290
660 to 810
Tensile Strength: Ultimate (UTS), MPa 500
1120 to 1390
Tensile Strength: Yield (Proof), MPa 500
1100 to 1340

Thermal Properties

Latent Heat of Fusion, J/g 410
390
Maximum Temperature: Mechanical, °C 170
430
Melting Completion (Liquidus), °C 640
1620
Melting Onset (Solidus), °C 600
1560
Specific Heat Capacity, J/kg-K 900
520
Thermal Conductivity, W/m-K 170
8.1
Thermal Expansion, µm/m-K 23
9.8

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 42
1.2
Electrical Conductivity: Equal Weight (Specific), % IACS 140
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
40
Density, g/cm3 2.8
4.8
Embodied Carbon, kg CO2/kg material 8.2
59
Embodied Energy, MJ/kg 150
950
Embodied Water, L/kg 1170
260

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 11
78 to 89
Stiffness to Weight: Axial, points 14
12
Stiffness to Weight: Bending, points 50
32
Strength to Weight: Axial, points 51
64 to 80
Strength to Weight: Bending, points 51
50 to 57
Thermal Diffusivity, mm2/s 67
3.2
Thermal Shock Resistance, points 22
79 to 98

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 94.4 to 98.4
2.5 to 3.5
Carbon (C), % 0
0 to 0.050
Chromium (Cr), % 0.040 to 0.25
2.5 to 3.5
Copper (Cu), % 0.2 to 0.7
0
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 0 to 0.8
0 to 0.25
Magnesium (Mg), % 0.5 to 1.1
0
Manganese (Mn), % 0.2 to 0.7
0
Nitrogen (N), % 0
0 to 0.050
Oxygen (O), % 0
0 to 0.13
Silicon (Si), % 0.7 to 1.5
0
Tin (Sn), % 0
2.5 to 3.5
Titanium (Ti), % 0 to 0.15
72.6 to 78.5
Vanadium (V), % 0
14 to 16
Zinc (Zn), % 0 to 0.3
0
Residuals, % 0 to 0.15
0 to 0.4