6110 Aluminum vs. Type 1 Niobium

6110 aluminum belongs to the aluminum alloys classification, while Type 1 niobium belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 6110 aluminum and the bottom bar is Type 1 niobium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 70
110
Elongation at Break, % 2.2
29
Poisson's Ratio 0.33
0.4
Shear Modulus, GPa 26
38
Tensile Strength: Ultimate (UTS), MPa 500
140
Tensile Strength: Yield (Proof), MPa 500
82

Thermal Properties

Latent Heat of Fusion, J/g 410
320
Specific Heat Capacity, J/kg-K 900
270
Thermal Conductivity, W/m-K 170
52
Thermal Expansion, µm/m-K 23
7.3

Otherwise Unclassified Properties

Density, g/cm3 2.8
8.6
Embodied Water, L/kg 1170
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 11
35
Resilience: Unit (Modulus of Resilience), kJ/m3 1770
32
Stiffness to Weight: Axial, points 14
6.8
Stiffness to Weight: Bending, points 50
18
Strength to Weight: Axial, points 51
4.6
Strength to Weight: Bending, points 51
7.1
Thermal Diffusivity, mm2/s 67
23
Thermal Shock Resistance, points 22
13

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 94.4 to 98.4
0
Carbon (C), % 0
0 to 0.010
Chromium (Cr), % 0.040 to 0.25
0
Copper (Cu), % 0.2 to 0.7
0
Hafnium (Hf), % 0
0 to 0.020
Hydrogen (H), % 0
0 to 0.0015
Iron (Fe), % 0 to 0.8
0 to 0.0050
Magnesium (Mg), % 0.5 to 1.1
0
Manganese (Mn), % 0.2 to 0.7
0
Molybdenum (Mo), % 0
0 to 0.010
Nickel (Ni), % 0
0 to 0.0050
Niobium (Nb), % 0
99.7 to 100
Nitrogen (N), % 0
0 to 0.010
Oxygen (O), % 0
0 to 0.015
Silicon (Si), % 0.7 to 1.5
0 to 0.0050
Tantalum (Ta), % 0
0 to 0.1
Titanium (Ti), % 0 to 0.15
0 to 0.020
Tungsten (W), % 0
0 to 0.030
Zinc (Zn), % 0 to 0.3
0
Zirconium (Zr), % 0
0 to 0.020
Residuals, % 0 to 0.15
0