6110 Aluminum vs. C93900 Bronze

6110 aluminum belongs to the aluminum alloys classification, while C93900 bronze belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 6110 aluminum and the bottom bar is C93900 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 70
95
Elongation at Break, % 2.2
5.6
Poisson's Ratio 0.33
0.36
Shear Modulus, GPa 26
35
Tensile Strength: Ultimate (UTS), MPa 500
190
Tensile Strength: Yield (Proof), MPa 500
130

Thermal Properties

Latent Heat of Fusion, J/g 410
170
Maximum Temperature: Mechanical, °C 170
140
Melting Completion (Liquidus), °C 640
940
Melting Onset (Solidus), °C 600
850
Specific Heat Capacity, J/kg-K 900
340
Thermal Conductivity, W/m-K 170
52
Thermal Expansion, µm/m-K 23
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 42
11
Electrical Conductivity: Equal Weight (Specific), % IACS 140
11

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
30
Density, g/cm3 2.8
9.1
Embodied Carbon, kg CO2/kg material 8.2
3.0
Embodied Energy, MJ/kg 150
49
Embodied Water, L/kg 1170
360

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 11
9.5
Resilience: Unit (Modulus of Resilience), kJ/m3 1770
83
Stiffness to Weight: Axial, points 14
5.8
Stiffness to Weight: Bending, points 50
17
Strength to Weight: Axial, points 51
5.9
Strength to Weight: Bending, points 51
8.1
Thermal Diffusivity, mm2/s 67
17
Thermal Shock Resistance, points 22
7.5

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 94.4 to 98.4
0 to 0.0050
Antimony (Sb), % 0
0 to 0.5
Chromium (Cr), % 0.040 to 0.25
0
Copper (Cu), % 0.2 to 0.7
76.5 to 79.5
Iron (Fe), % 0 to 0.8
0 to 0.4
Lead (Pb), % 0
14 to 18
Magnesium (Mg), % 0.5 to 1.1
0
Manganese (Mn), % 0.2 to 0.7
0
Nickel (Ni), % 0
0 to 0.8
Phosphorus (P), % 0
0 to 1.5
Silicon (Si), % 0.7 to 1.5
0 to 0.0050
Sulfur (S), % 0
0 to 0.080
Tin (Sn), % 0
5.0 to 7.0
Titanium (Ti), % 0 to 0.15
0
Zinc (Zn), % 0 to 0.3
0 to 1.5
Residuals, % 0 to 0.15
0 to 1.1