6110A Aluminum vs. 2017 Aluminum
Both 6110A aluminum and 2017 aluminum are aluminum alloys. They have a very high 96% of their average alloy composition in common.
For each property being compared, the top bar is 6110A aluminum and the bottom bar is 2017 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 71 |
| Elongation at Break, % | 11 to 18 | |
| 12 to 18 |
| Fatigue Strength, MPa | 140 to 210 | |
| 90 to 130 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 27 |
| Shear Strength, MPa | 220 to 280 | |
| 130 to 260 |
| Tensile Strength: Ultimate (UTS), MPa | 360 to 470 | |
| 190 to 430 |
| Tensile Strength: Yield (Proof), MPa | 250 to 430 | |
| 76 to 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 190 |
| Melting Completion (Liquidus), °C | 650 | |
| 640 |
| Melting Onset (Solidus), °C | 600 | |
| 510 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 880 |
| Thermal Conductivity, W/m-K | 160 | |
| 150 |
| Thermal Expansion, µm/m-K | 23 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 42 | |
| 38 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 140 | |
| 110 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 10 |
| Density, g/cm3 | 2.8 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 8.4 | |
| 8.0 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1170 | |
| 1140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 47 to 58 | |
| 24 to 66 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 450 to 1300 | |
| 41 to 470 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 50 | |
| 46 |
| Strength to Weight: Axial, points | 36 to 47 | |
| 17 to 40 |
| Strength to Weight: Bending, points | 41 to 48 | |
| 24 to 42 |
| Thermal Diffusivity, mm2/s | 65 | |
| 56 |
| Thermal Shock Resistance, points | 16 to 21 | |
| 7.9 to 18 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 94.8 to 98 | |
| 91.6 to 95.5 |
| Chromium (Cr), % | 0.050 to 0.25 | |
| 0 to 0.1 |
| Copper (Cu), % | 0.3 to 0.8 | |
| 3.5 to 4.5 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.7 |
| Magnesium (Mg), % | 0.7 to 1.1 | |
| 0.4 to 0.8 |
| Manganese (Mn), % | 0.3 to 0.9 | |
| 0.4 to 1.0 |
| Silicon (Si), % | 0.7 to 1.1 | |
| 0.2 to 0.8 |
| Titanium (Ti), % | 0 to 0.2 | |
| 0 to 0.15 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 to 0.25 |
| Zirconium (Zr), % | 0 to 0.2 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.15 |