6151 Aluminum vs. AS41B Magnesium
6151 aluminum belongs to the aluminum alloys classification, while AS41B magnesium belongs to the magnesium alloys.
For each property being compared, the top bar is 6151 aluminum and the bottom bar is AS41B magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 69 | |
| 45 |
| Elongation at Break, % | 1.1 to 5.7 | |
| 6.0 |
| Fatigue Strength, MPa | 80 to 100 | |
| 97 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 26 | |
| 18 |
| Shear Strength, MPa | 190 to 200 | |
| 120 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 340 | |
| 210 |
| Tensile Strength: Yield (Proof), MPa | 270 to 280 | |
| 140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 370 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 110 |
| Melting Completion (Liquidus), °C | 650 | |
| 620 |
| Melting Onset (Solidus), °C | 590 | |
| 570 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 1000 |
| Thermal Conductivity, W/m-K | 170 | |
| 68 |
| Thermal Expansion, µm/m-K | 23 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 45 | |
| 17 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 150 | |
| 92 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 12 |
| Density, g/cm3 | 2.7 | |
| 1.7 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 23 |
| Embodied Energy, MJ/kg | 150 | |
| 160 |
| Embodied Water, L/kg | 1180 | |
| 980 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 3.5 to 18 | |
| 11 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 520 to 580 | |
| 220 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 50 | |
| 72 |
| Strength to Weight: Axial, points | 34 | |
| 35 |
| Strength to Weight: Bending, points | 39 | |
| 47 |
| Thermal Diffusivity, mm2/s | 70 | |
| 41 |
| Thermal Shock Resistance, points | 15 | |
| 13 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 95.6 to 98.8 | |
| 3.5 to 5.0 |
| Chromium (Cr), % | 0.15 to 0.35 | |
| 0 |
| Copper (Cu), % | 0 to 0.35 | |
| 0 to 0.020 |
| Iron (Fe), % | 0 to 1.0 | |
| 0 to 0.0035 |
| Magnesium (Mg), % | 0.45 to 0.8 | |
| 92.7 to 95.7 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0.35 to 0.7 |
| Nickel (Ni), % | 0 | |
| 0 to 0.0020 |
| Silicon (Si), % | 0.6 to 1.2 | |
| 0.5 to 1.5 |
| Titanium (Ti), % | 0 to 0.15 | |
| 0 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 to 0.12 |
| Residuals, % | 0 to 0.15 | |
| 0 |