6262A Aluminum vs. AS41B Magnesium
6262A aluminum belongs to the aluminum alloys classification, while AS41B magnesium belongs to the magnesium alloys.
For each property being compared, the top bar is 6262A aluminum and the bottom bar is AS41B magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 45 |
| Elongation at Break, % | 4.5 to 11 | |
| 6.0 |
| Fatigue Strength, MPa | 94 to 110 | |
| 97 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 26 | |
| 18 |
| Shear Strength, MPa | 190 to 240 | |
| 120 |
| Tensile Strength: Ultimate (UTS), MPa | 310 to 410 | |
| 210 |
| Tensile Strength: Yield (Proof), MPa | 270 to 370 | |
| 140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 370 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 110 |
| Melting Completion (Liquidus), °C | 640 | |
| 620 |
| Melting Onset (Solidus), °C | 580 | |
| 570 |
| Specific Heat Capacity, J/kg-K | 890 | |
| 1000 |
| Thermal Conductivity, W/m-K | 170 | |
| 68 |
| Thermal Expansion, µm/m-K | 23 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 45 | |
| 17 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 140 | |
| 92 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 12 |
| Density, g/cm3 | 2.8 | |
| 1.7 |
| Embodied Carbon, kg CO2/kg material | 8.4 | |
| 23 |
| Embodied Energy, MJ/kg | 150 | |
| 160 |
| Embodied Water, L/kg | 1190 | |
| 980 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 17 to 34 | |
| 11 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 540 to 1000 | |
| 220 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 49 | |
| 72 |
| Strength to Weight: Axial, points | 31 to 41 | |
| 35 |
| Strength to Weight: Bending, points | 36 to 44 | |
| 47 |
| Thermal Diffusivity, mm2/s | 67 | |
| 41 |
| Thermal Shock Resistance, points | 14 to 18 | |
| 13 |
Alloy Composition
| Aluminum (Al), % | 94.2 to 97.8 | |
| 3.5 to 5.0 |
| Bismuth (Bi), % | 0.4 to 0.9 | |
| 0 |
| Chromium (Cr), % | 0.040 to 0.14 | |
| 0 |
| Copper (Cu), % | 0.15 to 0.4 | |
| 0 to 0.020 |
| Iron (Fe), % | 0 to 0.7 | |
| 0 to 0.0035 |
| Magnesium (Mg), % | 0.8 to 1.2 | |
| 92.7 to 95.7 |
| Manganese (Mn), % | 0 to 0.15 | |
| 0.35 to 0.7 |
| Nickel (Ni), % | 0 | |
| 0 to 0.0020 |
| Silicon (Si), % | 0.4 to 0.8 | |
| 0.5 to 1.5 |
| Tin (Sn), % | 0.4 to 1.0 | |
| 0 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 to 0.12 |
| Residuals, % | 0 to 0.15 | |
| 0 |