6360 Aluminum vs. 2030 Aluminum
Both 6360 aluminum and 2030 aluminum are aluminum alloys. They have a moderately high 93% of their average alloy composition in common.
For each property being compared, the top bar is 6360 aluminum and the bottom bar is 2030 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 70 |
| Elongation at Break, % | 9.0 to 18 | |
| 5.6 to 8.0 |
| Fatigue Strength, MPa | 31 to 67 | |
| 91 to 110 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 76 to 130 | |
| 220 to 250 |
| Tensile Strength: Ultimate (UTS), MPa | 120 to 220 | |
| 370 to 420 |
| Tensile Strength: Yield (Proof), MPa | 57 to 170 | |
| 240 to 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 190 |
| Melting Completion (Liquidus), °C | 640 | |
| 640 |
| Melting Onset (Solidus), °C | 630 | |
| 510 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 870 |
| Thermal Conductivity, W/m-K | 210 | |
| 130 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 54 | |
| 34 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 180 | |
| 99 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 10 |
| Density, g/cm3 | 2.7 | |
| 3.1 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 8.0 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1190 | |
| 1140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 14 to 19 | |
| 21 to 26 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 24 to 210 | |
| 390 to 530 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 50 | |
| 45 |
| Strength to Weight: Axial, points | 13 to 23 | |
| 33 to 38 |
| Strength to Weight: Bending, points | 20 to 30 | |
| 37 to 40 |
| Thermal Diffusivity, mm2/s | 86 | |
| 50 |
| Thermal Shock Resistance, points | 5.5 to 9.9 | |
| 16 to 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 97.8 to 99.3 | |
| 88.9 to 95.2 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.2 |
| Chromium (Cr), % | 0 to 0.050 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 to 0.15 | |
| 3.3 to 4.5 |
| Iron (Fe), % | 0.1 to 0.3 | |
| 0 to 0.7 |
| Lead (Pb), % | 0 | |
| 0.8 to 1.5 |
| Magnesium (Mg), % | 0.25 to 0.45 | |
| 0.5 to 1.3 |
| Manganese (Mn), % | 0.020 to 0.15 | |
| 0.2 to 1.0 |
| Silicon (Si), % | 0.35 to 0.8 | |
| 0 to 0.8 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 to 0.5 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.3 |