7005 Aluminum vs. 355.0 Aluminum
Both 7005 aluminum and 355.0 aluminum are aluminum alloys. They have a moderately high 94% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is 7005 aluminum and the bottom bar is 355.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 71 |
| Elongation at Break, % | 10 to 20 | |
| 1.5 to 2.6 |
| Fatigue Strength, MPa | 100 to 190 | |
| 55 to 70 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 27 |
| Shear Strength, MPa | 120 to 230 | |
| 150 to 240 |
| Tensile Strength: Ultimate (UTS), MPa | 200 to 400 | |
| 200 to 260 |
| Tensile Strength: Yield (Proof), MPa | 95 to 350 | |
| 150 to 190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 380 | |
| 470 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 180 |
| Melting Completion (Liquidus), °C | 640 | |
| 620 |
| Melting Onset (Solidus), °C | 610 | |
| 560 |
| Specific Heat Capacity, J/kg-K | 880 | |
| 890 |
| Thermal Conductivity, W/m-K | 140 to 170 | |
| 150 to 170 |
| Thermal Expansion, µm/m-K | 23 | |
| 22 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 35 to 43 | |
| 38 to 43 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 110 to 130 | |
| 120 to 140 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.9 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 8.0 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1150 | |
| 1120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 32 to 57 | |
| 2.7 to 5.9 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 65 to 850 | |
| 150 to 250 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 47 | |
| 51 |
| Strength to Weight: Axial, points | 19 to 38 | |
| 20 to 27 |
| Strength to Weight: Bending, points | 26 to 41 | |
| 28 to 33 |
| Thermal Diffusivity, mm2/s | 54 to 65 | |
| 60 to 69 |
| Thermal Shock Resistance, points | 8.7 to 18 | |
| 9.1 to 12 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 91 to 94.7 | |
| 90.3 to 94.1 |
| Chromium (Cr), % | 0.060 to 0.2 | |
| 0 to 0.25 |
| Copper (Cu), % | 0 to 0.1 | |
| 1.0 to 1.5 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 to 0.6 |
| Magnesium (Mg), % | 1.0 to 1.8 | |
| 0.4 to 0.6 |
| Manganese (Mn), % | 0.2 to 0.7 | |
| 0 to 0.5 |
| Silicon (Si), % | 0 to 0.35 | |
| 4.5 to 5.5 |
| Titanium (Ti), % | 0.010 to 0.060 | |
| 0 to 0.25 |
| Zinc (Zn), % | 4.0 to 5.0 | |
| 0 to 0.35 |
| Zirconium (Zr), % | 0.080 to 0.2 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.15 |