7020 Aluminum vs. 201.0 Aluminum
Both 7020 aluminum and 201.0 aluminum are aluminum alloys. They have a moderately high 94% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is 7020 aluminum and the bottom bar is 201.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 45 to 100 | |
| 95 to 140 |
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 71 |
| Elongation at Break, % | 8.4 to 14 | |
| 4.4 to 20 |
| Fatigue Strength, MPa | 110 to 130 | |
| 120 to 150 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 27 |
| Shear Strength, MPa | 110 to 230 | |
| 290 |
| Tensile Strength: Ultimate (UTS), MPa | 190 to 390 | |
| 370 to 470 |
| Tensile Strength: Yield (Proof), MPa | 120 to 310 | |
| 220 to 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 380 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 170 |
| Melting Completion (Liquidus), °C | 650 | |
| 650 |
| Melting Onset (Solidus), °C | 610 | |
| 570 |
| Specific Heat Capacity, J/kg-K | 880 | |
| 870 |
| Thermal Conductivity, W/m-K | 150 | |
| 120 |
| Thermal Expansion, µm/m-K | 23 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 39 | |
| 30 to 33 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 | |
| 87 to 97 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 38 |
| Density, g/cm3 | 2.9 | |
| 3.1 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 8.7 |
| Embodied Energy, MJ/kg | 150 | |
| 160 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 23 to 46 | |
| 19 to 63 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 to 690 | |
| 330 to 1160 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 47 | |
| 45 |
| Strength to Weight: Axial, points | 18 to 37 | |
| 33 to 42 |
| Strength to Weight: Bending, points | 25 to 41 | |
| 37 to 44 |
| Thermal Diffusivity, mm2/s | 59 | |
| 45 |
| Thermal Shock Resistance, points | 8.3 to 17 | |
| 19 to 25 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 91.2 to 94.8 | |
| 92.1 to 95.1 |
| Chromium (Cr), % | 0.1 to 0.35 | |
| 0 |
| Copper (Cu), % | 0 to 0.2 | |
| 4.0 to 5.2 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 to 0.15 |
| Magnesium (Mg), % | 1.0 to 1.4 | |
| 0.15 to 0.55 |
| Manganese (Mn), % | 0.050 to 0.5 | |
| 0.2 to 0.5 |
| Silicon (Si), % | 0 to 0.35 | |
| 0 to 0.1 |
| Silver (Ag), % | 0 | |
| 0.4 to 1.0 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0.15 to 0.35 |
| Zinc (Zn), % | 4.0 to 5.0 | |
| 0 |
| Zirconium (Zr), % | 0.080 to 0.25 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.1 |