7021 Aluminum vs. 6262A Aluminum

Both 7021 aluminum and 6262A aluminum are aluminum alloys. They have a moderately high 94% of their average alloy composition in common.

For each property being compared, the top bar is 7021 aluminum and the bottom bar is 6262A aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 69
68
Elongation at Break, % 9.4
4.5 to 11
Fatigue Strength, MPa 150
94 to 110
Poisson's Ratio 0.32
0.33
Shear Modulus, GPa 26
26
Shear Strength, MPa 270
190 to 240
Tensile Strength: Ultimate (UTS), MPa 460
310 to 410
Tensile Strength: Yield (Proof), MPa 390
270 to 370

Thermal Properties

Latent Heat of Fusion, J/g 380
400
Maximum Temperature: Mechanical, °C 200
160
Melting Completion (Liquidus), °C 630
640
Melting Onset (Solidus), °C 510
580
Specific Heat Capacity, J/kg-K 870
890
Thermal Conductivity, W/m-K 150
170
Thermal Expansion, µm/m-K 24
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 38
45
Electrical Conductivity: Equal Weight (Specific), % IACS 120
140

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
11
Density, g/cm3 2.9
2.8
Embodied Carbon, kg CO2/kg material 8.3
8.4
Embodied Energy, MJ/kg 150
150
Embodied Water, L/kg 1140
1190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 41
17 to 34
Resilience: Unit (Modulus of Resilience), kJ/m3 1110
540 to 1000
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 47
49
Strength to Weight: Axial, points 44
31 to 41
Strength to Weight: Bending, points 45
36 to 44
Thermal Diffusivity, mm2/s 59
67
Thermal Shock Resistance, points 20
14 to 18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 90.7 to 93.7
94.2 to 97.8
Bismuth (Bi), % 0
0.4 to 0.9
Chromium (Cr), % 0 to 0.050
0.040 to 0.14
Copper (Cu), % 0 to 0.25
0.15 to 0.4
Iron (Fe), % 0 to 0.4
0 to 0.7
Magnesium (Mg), % 1.2 to 1.8
0.8 to 1.2
Manganese (Mn), % 0 to 0.1
0 to 0.15
Silicon (Si), % 0 to 0.25
0.4 to 0.8
Tin (Sn), % 0
0.4 to 1.0
Titanium (Ti), % 0 to 0.1
0 to 0.1
Zinc (Zn), % 5.0 to 6.0
0 to 0.25
Zirconium (Zr), % 0.080 to 0.18
0
Residuals, % 0 to 0.15
0 to 0.15