7050 Aluminum vs. EN AC-71100 Aluminum
Both 7050 aluminum and EN AC-71100 aluminum are aluminum alloys. They have 88% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is 7050 aluminum and the bottom bar is EN AC-71100 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 72 |
| Elongation at Break, % | 2.2 to 12 | |
| 1.1 |
| Fatigue Strength, MPa | 130 to 210 | |
| 150 |
| Poisson's Ratio | 0.32 | |
| 0.32 |
| Shear Modulus, GPa | 26 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 490 to 570 | |
| 260 |
| Tensile Strength: Yield (Proof), MPa | 390 to 500 | |
| 230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 490 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 170 |
| Melting Completion (Liquidus), °C | 630 | |
| 580 |
| Melting Onset (Solidus), °C | 490 | |
| 520 |
| Specific Heat Capacity, J/kg-K | 860 | |
| 860 |
| Thermal Expansion, µm/m-K | 24 | |
| 22 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 35 | |
| 32 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 100 | |
| 97 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 9.5 |
| Density, g/cm3 | 3.1 | |
| 2.9 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 7.4 |
| Embodied Energy, MJ/kg | 150 | |
| 140 |
| Embodied Water, L/kg | 1120 | |
| 1010 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 10 to 55 | |
| 2.8 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1110 to 1760 | |
| 360 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 45 | |
| 47 |
| Strength to Weight: Axial, points | 45 to 51 | |
| 25 |
| Strength to Weight: Bending, points | 45 to 50 | |
| 31 |
| Thermal Shock Resistance, points | 21 to 25 | |
| 12 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 87.3 to 92.1 | |
| 78.7 to 83.3 |
| Chromium (Cr), % | 0 to 0.040 | |
| 0 |
| Copper (Cu), % | 2.0 to 2.6 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.15 | |
| 0 to 0.3 |
| Magnesium (Mg), % | 1.9 to 2.6 | |
| 0.2 to 0.5 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 to 0.15 |
| Silicon (Si), % | 0 to 0.12 | |
| 7.5 to 9.5 |
| Titanium (Ti), % | 0 to 0.060 | |
| 0 to 0.15 |
| Zinc (Zn), % | 5.7 to 6.7 | |
| 9.0 to 10.5 |
| Zirconium (Zr), % | 0.080 to 0.15 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.15 |