7175 Aluminum vs. 2011 Aluminum
Both 7175 aluminum and 2011 aluminum are aluminum alloys. They have a moderately high 92% of their average alloy composition in common.
For each property being compared, the top bar is 7175 aluminum and the bottom bar is 2011 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 71 |
| Elongation at Break, % | 3.8 to 5.9 | |
| 8.5 to 18 |
| Fatigue Strength, MPa | 150 to 180 | |
| 74 to 120 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 27 |
| Shear Strength, MPa | 290 to 330 | |
| 190 to 250 |
| Tensile Strength: Ultimate (UTS), MPa | 520 to 570 | |
| 310 to 420 |
| Tensile Strength: Yield (Proof), MPa | 430 to 490 | |
| 140 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 380 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 190 |
| Melting Completion (Liquidus), °C | 640 | |
| 640 |
| Melting Onset (Solidus), °C | 480 | |
| 540 |
| Specific Heat Capacity, J/kg-K | 870 | |
| 870 |
| Thermal Conductivity, W/m-K | 140 | |
| 140 to 170 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 33 | |
| 35 to 45 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 99 | |
| 100 to 130 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 11 |
| Density, g/cm3 | 3.0 | |
| 3.1 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 7.9 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1130 | |
| 1150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 18 to 29 | |
| 29 to 52 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1310 to 1730 | |
| 140 to 680 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 46 | |
| 44 |
| Strength to Weight: Axial, points | 48 to 52 | |
| 27 to 37 |
| Strength to Weight: Bending, points | 48 to 51 | |
| 32 to 40 |
| Thermal Diffusivity, mm2/s | 53 | |
| 51 to 64 |
| Thermal Shock Resistance, points | 23 to 25 | |
| 14 to 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 88 to 91.4 | |
| 91.3 to 94.6 |
| Bismuth (Bi), % | 0 | |
| 0.2 to 0.6 |
| Chromium (Cr), % | 0.18 to 0.28 | |
| 0 |
| Copper (Cu), % | 1.2 to 2.0 | |
| 5.0 to 6.0 |
| Iron (Fe), % | 0 to 0.2 | |
| 0 to 0.7 |
| Lead (Pb), % | 0 | |
| 0.2 to 0.6 |
| Magnesium (Mg), % | 2.1 to 2.9 | |
| 0 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 |
| Silicon (Si), % | 0 to 0.15 | |
| 0 to 0.4 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 |
| Zinc (Zn), % | 5.1 to 6.1 | |
| 0 to 0.3 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.15 |