8090 Aluminum vs. 3103 Aluminum

Both 8090 aluminum and 3103 aluminum are aluminum alloys. They have a very high 97% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is 8090 aluminum and the bottom bar is 3103 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 67
70
Elongation at Break, % 3.5 to 13
1.1 to 28
Fatigue Strength, MPa 91 to 140
38 to 83
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 25
26
Tensile Strength: Ultimate (UTS), MPa 340 to 490
100 to 220
Tensile Strength: Yield (Proof), MPa 210 to 420
39 to 200

Thermal Properties

Latent Heat of Fusion, J/g 400
400
Maximum Temperature: Mechanical, °C 190
190
Melting Completion (Liquidus), °C 660
660
Melting Onset (Solidus), °C 600
640
Specific Heat Capacity, J/kg-K 960
900
Thermal Conductivity, W/m-K 95 to 160
160
Thermal Expansion, µm/m-K 24
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 20
42
Electrical Conductivity: Equal Weight (Specific), % IACS 66
140

Otherwise Unclassified Properties

Base Metal Price, % relative 18
9.5
Density, g/cm3 2.7
2.8
Embodied Carbon, kg CO2/kg material 8.6
8.2
Embodied Energy, MJ/kg 170
150
Embodied Water, L/kg 1160
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 16 to 41
2.4 to 24
Resilience: Unit (Modulus of Resilience), kJ/m3 340 to 1330
11 to 280
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 50
50
Strength to Weight: Axial, points 34 to 49
10 to 22
Strength to Weight: Bending, points 39 to 50
18 to 30
Thermal Diffusivity, mm2/s 36 to 60
64
Thermal Shock Resistance, points 15 to 22
4.6 to 9.9

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 93 to 98.4
96.3 to 99.1
Chromium (Cr), % 0 to 0.1
0 to 0.1
Copper (Cu), % 1.0 to 1.6
0 to 0.1
Iron (Fe), % 0 to 0.3
0 to 0.7
Lithium (Li), % 2.2 to 2.7
0
Magnesium (Mg), % 0.6 to 1.3
0 to 0.3
Manganese (Mn), % 0 to 0.1
0.9 to 1.5
Silicon (Si), % 0 to 0.2
0 to 0.5
Titanium (Ti), % 0 to 0.1
0 to 0.1
Zinc (Zn), % 0 to 0.25
0 to 0.2
Zirconium (Zr), % 0.040 to 0.16
0 to 0.1
Residuals, % 0 to 0.15
0 to 0.15