MakeItFrom.com
Menu (ESC)

8090 Aluminum vs. EN 1.0566 Steel

8090 aluminum belongs to the aluminum alloys classification, while EN 1.0566 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 8090 aluminum and the bottom bar is EN 1.0566 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 67
190
Elongation at Break, % 3.5 to 13
24
Fatigue Strength, MPa 91 to 140
270
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 25
73
Tensile Strength: Ultimate (UTS), MPa 340 to 490
550
Tensile Strength: Yield (Proof), MPa 210 to 420
370

Thermal Properties

Latent Heat of Fusion, J/g 400
250
Maximum Temperature: Mechanical, °C 190
400
Melting Completion (Liquidus), °C 660
1460
Melting Onset (Solidus), °C 600
1420
Specific Heat Capacity, J/kg-K 960
470
Thermal Conductivity, W/m-K 95 to 160
50
Thermal Expansion, µm/m-K 24
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 20
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 66
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 18
2.3
Density, g/cm3 2.7
7.8
Embodied Carbon, kg CO2/kg material 8.6
1.6
Embodied Energy, MJ/kg 170
22
Embodied Water, L/kg 1160
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 16 to 41
120
Resilience: Unit (Modulus of Resilience), kJ/m3 340 to 1330
360
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 50
24
Strength to Weight: Axial, points 34 to 49
19
Strength to Weight: Bending, points 39 to 50
19
Thermal Diffusivity, mm2/s 36 to 60
14
Thermal Shock Resistance, points 15 to 22
17

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 93 to 98.4
0.020 to 0.024
Carbon (C), % 0
0 to 0.18
Chromium (Cr), % 0 to 0.1
0 to 0.3
Copper (Cu), % 1.0 to 1.6
0 to 0.3
Iron (Fe), % 0 to 0.3
96.2 to 98.9
Lithium (Li), % 2.2 to 2.7
0
Magnesium (Mg), % 0.6 to 1.3
0
Manganese (Mn), % 0 to 0.1
1.1 to 1.7
Molybdenum (Mo), % 0
0 to 0.080
Nickel (Ni), % 0
0 to 0.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 0.2
0 to 0.5
Sulfur (S), % 0
0 to 0.0080
Titanium (Ti), % 0 to 0.1
0 to 0.030
Vanadium (V), % 0
0 to 0.1
Zinc (Zn), % 0 to 0.25
0
Zirconium (Zr), % 0.040 to 0.16
0
Residuals, % 0 to 0.15
0