85-platinum 15-iridium vs. ASTM B540 Palladium
Both 85-platinum 15-iridium and ASTM B540 palladium are otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is 85-platinum 15-iridium and the bottom bar is ASTM B540 palladium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 110 |
| Elongation at Break, % | 5.5 to 34 | |
| 1.1 to 14 |
| Poisson's Ratio | 0.38 | |
| 0.38 |
| Shear Modulus, GPa | 81 | |
| 39 |
| Shear Strength, MPa | 370 to 420 | |
| 500 to 700 |
| Tensile Strength: Ultimate (UTS), MPa | 560 to 730 | |
| 830 to 1240 |
Thermal Properties
| Latent Heat of Fusion, J/g | 110 | |
| 140 |
| Melting Completion (Liquidus), °C | 1820 | |
| 1220 |
| Melting Onset (Solidus), °C | 1790 | |
| 1020 |
| Specific Heat Capacity, J/kg-K | 130 | |
| 240 |
| Thermal Expansion, µm/m-K | 8.4 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 6.2 | |
| 4.9 to 5.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.6 | |
| 3.5 to 3.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 22 | |
| 13 |
Common Calculations
| Stiffness to Weight: Axial, points | 5.7 | |
| 4.7 |
| Stiffness to Weight: Bending, points | 9.3 | |
| 12 |
| Strength to Weight: Axial, points | 7.1 to 9.3 | |
| 18 to 27 |
| Strength to Weight: Bending, points | 6.9 to 8.3 | |
| 15 to 20 |
| Thermal Shock Resistance, points | 21 to 28 | |
| 41 to 61 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 0 | |
| 13.5 to 14.5 |
| Gold (Au), % | 0 | |
| 9.5 to 10.5 |
| Iridium (Ir), % | 14.5 to 15.5 | |
| 0 |
| Palladium (Pd), % | 0 | |
| 34 to 36 |
| Platinum (Pt), % | 84.3 to 85.5 | |
| 9.5 to 10.5 |
| Silver (Ag), % | 0 | |
| 29 to 31 |
| Zinc (Zn), % | 0 | |
| 0.8 to 1.2 |
| Residuals, % | 0 to 0.2 | |
| 0 to 0.3 |