85-silver 15-nickel vs. 70Ag-30Ni Alloy
Both 85-silver 15-nickel and 70Ag-30Ni alloy are otherwise unclassified metals. They have 85% of their average alloy composition in common.
For each property being compared, the top bar is 85-silver 15-nickel and the bottom bar is 70Ag-30Ni alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 88 | |
| 100 |
| Poisson's Ratio | 0.36 | |
| 0.35 |
| Shear Modulus, GPa | 32 | |
| 39 |
| Tensile Strength: Ultimate (UTS), MPa | 260 to 470 | |
| 320 to 530 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 170 |
| Melting Completion (Liquidus), °C | 870 | |
| 960 |
| Melting Onset (Solidus), °C | 960 | |
| 960 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 300 |
| Thermal Expansion, µm/m-K | 18 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 86 | |
| 69 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 75 | |
| 62 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 10 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.8 | |
| 5.8 |
| Stiffness to Weight: Bending, points | 14 | |
| 16 |
| Strength to Weight: Axial, points | 7.1 to 13 | |
| 8.8 to 15 |
| Strength to Weight: Bending, points | 8.9 to 13 | |
| 10 to 15 |
| Thermal Shock Resistance, points | 12 to 21 | |
| 13 to 21 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Nickel (Ni), % | 13.8 to 16 | |
| 28.8 to 31 |
| Silver (Ag), % | 84 to 86 | |
| 69 to 71 |
| Residuals, % | 0 to 0.2 | |
| 0 to 0.2 |