85-silver 15-nickel vs. Solder Alloy 715

Both 85-silver 15-nickel and solder alloy 715 are otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is 85-silver 15-nickel and the bottom bar is solder alloy 715.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 88
51
Poisson's Ratio 0.36
0.36
Shear Modulus, GPa 32
19
Tensile Strength: Ultimate (UTS), MPa 260 to 470
30

Thermal Properties

Latent Heat of Fusion, J/g 140
61
Melting Completion (Liquidus), °C 870
220
Melting Onset (Solidus), °C 960
220
Specific Heat Capacity, J/kg-K 270
220
Thermal Expansion, µm/m-K 18
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 86
12
Electrical Conductivity: Equal Weight (Specific), % IACS 75
15

Otherwise Unclassified Properties

Density, g/cm3 10
7.3

Common Calculations

Stiffness to Weight: Axial, points 4.8
3.8
Stiffness to Weight: Bending, points 14
17
Strength to Weight: Axial, points 7.1 to 13
1.1
Strength to Weight: Bending, points 8.9 to 13
2.9
Thermal Shock Resistance, points 12 to 21
1.9

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Copper (Cu), % 0
0.5 to 0.9
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0
0 to 0.020
Lead (Pb), % 0
0 to 0.070
Nickel (Ni), % 13.8 to 16
0 to 0.010
Silver (Ag), % 84 to 86
0.8 to 1.2
Tin (Sn), % 0
97.4 to 98.7
Zinc (Zn), % 0
0 to 0.0010
Residuals, % 0 to 0.2
0