85-silver 15-nickel vs. Type 2 Pewter
Both 85-silver 15-nickel and Type 2 pewter are otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is 85-silver 15-nickel and the bottom bar is Type 2 pewter.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 88 | |
| 52 |
| Poisson's Ratio | 0.36 | |
| 0.35 |
| Shear Modulus, GPa | 32 | |
| 19 |
| Tensile Strength: Ultimate (UTS), MPa | 260 to 470 | |
| 52 to 68 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 69 |
| Melting Completion (Liquidus), °C | 870 | |
| 300 |
| Melting Onset (Solidus), °C | 960 | |
| 240 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 220 |
| Thermal Expansion, µm/m-K | 18 | |
| 21 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 7.3 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.8 | |
| 3.9 |
| Stiffness to Weight: Bending, points | 14 | |
| 17 |
| Strength to Weight: Axial, points | 7.1 to 13 | |
| 2.0 to 2.6 |
| Strength to Weight: Bending, points | 8.9 to 13 | |
| 4.3 to 5.1 |
| Thermal Shock Resistance, points | 12 to 21 | |
| 3.4 to 4.4 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Antimony (Sb), % | 0 | |
| 5.0 to 7.5 |
| Arsenic (As), % | 0 | |
| 0 to 0.050 |
| Copper (Cu), % | 0 | |
| 1.5 to 3.0 |
| Iron (Fe), % | 0 | |
| 0 to 0.015 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Nickel (Ni), % | 13.8 to 16 | |
| 0 |
| Silver (Ag), % | 84 to 86 | |
| 0 |
| Tin (Sn), % | 0 | |
| 90 to 93 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0050 |
| Residuals, % | 0 to 0.2 | |
| 0 |