85-silver 15-nickel vs. S45503 Stainless Steel
85-silver 15-nickel belongs to the otherwise unclassified metals classification, while S45503 stainless steel belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is 85-silver 15-nickel and the bottom bar is S45503 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 88 | |
| 190 |
| Poisson's Ratio | 0.36 | |
| 0.28 |
| Shear Modulus, GPa | 32 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 260 to 470 | |
| 1610 to 1850 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 270 |
| Melting Completion (Liquidus), °C | 870 | |
| 1440 |
| Melting Onset (Solidus), °C | 960 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 470 |
| Thermal Expansion, µm/m-K | 18 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 7.9 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.8 | |
| 14 |
| Stiffness to Weight: Bending, points | 14 | |
| 24 |
| Strength to Weight: Axial, points | 7.1 to 13 | |
| 57 to 65 |
| Strength to Weight: Bending, points | 8.9 to 13 | |
| 39 to 43 |
| Thermal Shock Resistance, points | 12 to 21 | |
| 56 to 64 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 | |
| 0 to 0.010 |
| Chromium (Cr), % | 0 | |
| 11 to 12.5 |
| Copper (Cu), % | 0 | |
| 1.5 to 2.5 |
| Iron (Fe), % | 0 | |
| 72.4 to 78.9 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 13.8 to 16 | |
| 7.5 to 9.5 |
| Niobium (Nb), % | 0 | |
| 0.1 to 0.5 |
| Phosphorus (P), % | 0 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 | |
| 0 to 0.2 |
| Silver (Ag), % | 84 to 86 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 1.0 to 1.4 |
| Residuals, % | 0 to 0.2 | |
| 0 |