852.0 Aluminum vs. 713.0 Aluminum
Both 852.0 aluminum and 713.0 aluminum are aluminum alloys. They have a moderately high 91% of their average alloy composition in common.
For each property being compared, the top bar is 852.0 aluminum and the bottom bar is 713.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 64 | |
| 74 to 75 |
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 71 |
| Elongation at Break, % | 3.4 | |
| 3.9 to 4.3 |
| Fatigue Strength, MPa | 73 | |
| 63 to 120 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Shear Modulus, GPa | 26 | |
| 27 |
| Shear Strength, MPa | 130 | |
| 180 |
| Tensile Strength: Ultimate (UTS), MPa | 200 | |
| 240 to 260 |
| Tensile Strength: Yield (Proof), MPa | 150 | |
| 170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 370 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 180 |
| Melting Completion (Liquidus), °C | 640 | |
| 630 |
| Melting Onset (Solidus), °C | 210 | |
| 610 |
| Solidification (Pattern Maker's) Shrinkage, % | 1.3 | |
| 1.6 |
| Specific Heat Capacity, J/kg-K | 840 | |
| 860 |
| Thermal Conductivity, W/m-K | 180 | |
| 150 |
| Thermal Expansion, µm/m-K | 23 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 45 | |
| 35 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 130 | |
| 100 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 9.5 |
| Density, g/cm3 | 3.2 | |
| 3.1 |
| Embodied Carbon, kg CO2/kg material | 8.5 | |
| 7.8 |
| Embodied Energy, MJ/kg | 160 | |
| 150 |
| Embodied Water, L/kg | 1150 | |
| 1110 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.2 | |
| 8.7 to 9.9 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 160 | |
| 210 to 220 |
| Stiffness to Weight: Axial, points | 12 | |
| 13 |
| Stiffness to Weight: Bending, points | 43 | |
| 45 |
| Strength to Weight: Axial, points | 17 | |
| 22 to 23 |
| Strength to Weight: Bending, points | 24 | |
| 28 to 29 |
| Thermal Diffusivity, mm2/s | 65 | |
| 57 |
| Thermal Shock Resistance, points | 8.7 | |
| 10 to 11 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 86.6 to 91.3 | |
| 87.6 to 92.4 |
| Chromium (Cr), % | 0 | |
| 0 to 0.35 |
| Copper (Cu), % | 1.7 to 2.3 | |
| 0.4 to 1.0 |
| Iron (Fe), % | 0 to 0.7 | |
| 0 to 1.1 |
| Magnesium (Mg), % | 0.6 to 0.9 | |
| 0.2 to 0.5 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 to 0.6 |
| Nickel (Ni), % | 0.9 to 1.5 | |
| 0 to 0.15 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 0.25 |
| Tin (Sn), % | 5.5 to 7.0 | |
| 0 |
| Titanium (Ti), % | 0 to 0.2 | |
| 0 to 0.25 |
| Zinc (Zn), % | 0 | |
| 7.0 to 8.0 |
| Residuals, % | 0 to 0.3 | |
| 0 to 0.25 |