852.0 Aluminum vs. SAE-AISI 1340 Steel
852.0 aluminum belongs to the aluminum alloys classification, while SAE-AISI 1340 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 852.0 aluminum and the bottom bar is SAE-AISI 1340 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 64 | |
| 160 to 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 190 |
| Elongation at Break, % | 3.4 | |
| 11 to 23 |
| Fatigue Strength, MPa | 73 | |
| 220 to 390 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 26 | |
| 72 |
| Shear Strength, MPa | 130 | |
| 340 to 440 |
| Tensile Strength: Ultimate (UTS), MPa | 200 | |
| 540 to 730 |
| Tensile Strength: Yield (Proof), MPa | 150 | |
| 300 to 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 400 |
| Melting Completion (Liquidus), °C | 640 | |
| 1450 |
| Melting Onset (Solidus), °C | 210 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 840 | |
| 470 |
| Thermal Conductivity, W/m-K | 180 | |
| 51 |
| Thermal Expansion, µm/m-K | 23 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 45 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 130 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 1.9 |
| Density, g/cm3 | 3.2 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 8.5 | |
| 1.4 |
| Embodied Energy, MJ/kg | 160 | |
| 19 |
| Embodied Water, L/kg | 1150 | |
| 48 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.2 | |
| 78 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 160 | |
| 240 to 1040 |
| Stiffness to Weight: Axial, points | 12 | |
| 13 |
| Stiffness to Weight: Bending, points | 43 | |
| 24 |
| Strength to Weight: Axial, points | 17 | |
| 19 to 26 |
| Strength to Weight: Bending, points | 24 | |
| 19 to 23 |
| Thermal Diffusivity, mm2/s | 65 | |
| 14 |
| Thermal Shock Resistance, points | 8.7 | |
| 17 to 23 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 86.6 to 91.3 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.38 to 0.43 |
| Copper (Cu), % | 1.7 to 2.3 | |
| 0 |
| Iron (Fe), % | 0 to 0.7 | |
| 97.2 to 97.9 |
| Magnesium (Mg), % | 0.6 to 0.9 | |
| 0 |
| Manganese (Mn), % | 0 to 0.1 | |
| 1.6 to 1.9 |
| Nickel (Ni), % | 0.9 to 1.5 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 to 0.4 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 | |
| 0 to 0.040 |
| Tin (Sn), % | 5.5 to 7.0 | |
| 0 |
| Titanium (Ti), % | 0 to 0.2 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 |