86.5-silver 13.5-cadmium-oxide vs. Grade 200 Maraging Steel
86.5-silver 13.5-cadmium-oxide belongs to the otherwise unclassified metals classification, while grade 200 maraging steel belongs to the iron alloys. There are 6 material properties with values for both materials. Properties with values for just one material (23, in this case) are not shown.
For each property being compared, the top bar is 86.5-silver 13.5-cadmium-oxide and the bottom bar is grade 200 maraging steel.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 10 | |
| 8.2 |
| Elongation at Break, % | 3.4 to 16 | |
| 9.1 to 18 |
| Shear Strength, MPa | 170 to 210 | |
| 600 to 890 |
| Strength to Weight: Axial, points | 7.6 to 11 | |
| 33 to 51 |
| Strength to Weight: Bending, points | 9.3 to 12 | |
| 27 to 35 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 410 | |
| 970 to 1500 |