86.5-silver 13.5-cadmium-oxide vs. Z13004 Zinc
86.5-silver 13.5-cadmium-oxide belongs to the otherwise unclassified metals classification, while Z13004 zinc belongs to the zinc alloys. There are 7 material properties with values for both materials. Properties with values for just one material (22, in this case) are not shown.
For each property being compared, the top bar is 86.5-silver 13.5-cadmium-oxide and the bottom bar is Z13004 zinc.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 10 | |
| 6.6 |
| Electrical Conductivity: Equal Volume, % IACS | 72 to 85 | |
| 27 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 64 to 76 | |
| 37 |
| Elongation at Break, % | 3.4 to 16 | |
| 30 |
| Strength to Weight: Axial, points | 7.6 to 11 | |
| 3.9 |
| Strength to Weight: Bending, points | 9.3 to 12 | |
| 7.0 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 410 | |
| 93 |