88-silver 12-tin-oxide vs. C14500 Copper
88-silver 12-tin-oxide belongs to the otherwise unclassified metals classification, while C14500 copper belongs to the copper alloys. There are 6 material properties with values for both materials. Properties with values for just one material (24, in this case) are not shown.
For each property being compared, the top bar is 88-silver 12-tin-oxide and the bottom bar is C14500 copper.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 84 to 86 | |
| 94 |
| Elongation at Break, % | 9.0 to 37 | |
| 12 to 50 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 24 to 70 | |
| 36 to 85 |
| Shear Strength, MPa | 150 to 160 | |
| 150 to 190 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 280 | |
| 220 to 330 |
| Tensile Strength: Yield (Proof), MPa | 110 to 260 | |
| 69 to 260 |