88-silver 12-tin-oxide vs. C26200 Brass
88-silver 12-tin-oxide belongs to the otherwise unclassified metals classification, while C26200 brass belongs to the copper alloys. There are 6 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is 88-silver 12-tin-oxide and the bottom bar is C26200 brass.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 84 to 86 | |
| 28 |
| Elongation at Break, % | 9.0 to 37 | |
| 3.0 to 180 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 24 to 70 | |
| 19 to 160 |
| Shear Strength, MPa | 150 to 160 | |
| 230 to 390 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 280 | |
| 330 to 770 |
| Tensile Strength: Yield (Proof), MPa | 110 to 260 | |
| 110 to 490 |