88-silver 12-tin-oxide vs. C41500 Brass
88-silver 12-tin-oxide belongs to the otherwise unclassified metals classification, while C41500 brass belongs to the copper alloys. There are 6 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is 88-silver 12-tin-oxide and the bottom bar is C41500 brass.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 84 to 86 | |
| 28 |
| Elongation at Break, % | 9.0 to 37 | |
| 2.0 to 42 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 24 to 70 | |
| 11 to 120 |
| Shear Strength, MPa | 150 to 160 | |
| 220 to 360 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 280 | |
| 340 to 560 |
| Tensile Strength: Yield (Proof), MPa | 110 to 260 | |
| 190 to 550 |