90-platinum 10-iridium vs. ASTM B617 Coin Silver
Both 90-platinum 10-iridium and ASTM B617 coin silver are otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 90-platinum 10-iridium and the bottom bar is ASTM B617 coin silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 75 |
| Elongation at Break, % | 5.5 to 34 | |
| 1.1 to 22 |
| Poisson's Ratio | 0.38 | |
| 0.37 |
| Shear Modulus, GPa | 74 | |
| 28 |
| Shear Strength, MPa | 220 to 320 | |
| 180 to 290 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 550 | |
| 290 to 520 |
Thermal Properties
| Latent Heat of Fusion, J/g | 100 | |
| 120 |
| Specific Heat Capacity, J/kg-K | 130 | |
| 250 |
| Thermal Expansion, µm/m-K | 8.6 | |
| 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 22 | |
| 10 |
Common Calculations
| Stiffness to Weight: Axial, points | 5.3 | |
| 4.1 |
| Stiffness to Weight: Bending, points | 9.1 | |
| 14 |
| Strength to Weight: Axial, points | 4.2 to 7.1 | |
| 7.7 to 14 |
| Strength to Weight: Bending, points | 4.9 to 6.9 | |
| 9.3 to 14 |
| Thermal Shock Resistance, points | 13 to 22 | |
| 14 to 25 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.050 |
| Copper (Cu), % | 0 | |
| 9.0 to 10.4 |
| Iridium (Ir), % | 9.5 to 10.5 | |
| 0 |
| Iron (Fe), % | 0 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 | |
| 0 to 0.030 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Phosphorus (P), % | 0 | |
| 0 to 0.020 |
| Platinum (Pt), % | 89.3 to 90.5 | |
| 0 |
| Silver (Ag), % | 0 | |
| 89.6 to 91 |
| Zinc (Zn), % | 0 | |
| 0 to 0.060 |
| Residuals, % | 0 to 0.2 | |
| 0 to 0.060 |