90-silver 10-tin-oxide vs. ISO-WD21150 Magnesium
90-silver 10-tin-oxide belongs to the otherwise unclassified metals classification, while ISO-WD21150 magnesium belongs to the magnesium alloys. There are 6 material properties with values for both materials. Properties with values for just one material (23, in this case) are not shown.
For each property being compared, the top bar is 90-silver 10-tin-oxide and the bottom bar is ISO-WD21150 magnesium.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 77 to 82 | |
| 19 |
| Elongation at Break, % | 7.0 to 35 | |
| 5.7 to 11 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 20 to 68 | |
| 15 to 24 |
| Shear Strength, MPa | 160 to 170 | |
| 150 to 170 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 300 | |
| 240 to 290 |
| Tensile Strength: Yield (Proof), MPa | 120 to 280 | |
| 120 to 200 |